DW350-50优质硅钢

电工钢硅钢片因此各国生产电工钢板总是千方百计设法降低铁损，并以铁损作为考核产品磁性的重要指标，按产品的铁损值作为划分产品牌号的依据。冷轧取向电工钢：冷轧取向电工钢是电工钢中的高端产品，与冷轧无取向电工钢相比，磁性具有强烈的方向性；在易磁化的轧制方向上具有优越的高磁导率与低损耗特性。取向钢带在轧制方向的铁损仅为横向的1/3，磁导率之比为6：1。用途：冷轧取向硅钢带主要的用途是用于变压器制造。全工艺冷轧无取向硅钢涂层：全工艺冷轧硅钢表面涂有一层半透明的绝缘涂层，在不同的标准中有不同的代码，我们以宝钢的Q/BQB 480 2014为例：

电工钢硅钢片 磁感应强度B磁感应强度又称磁通密度，是衡量磁性材料单位面积磁化能力的技术指标。磁感应强度提高，意味着铁芯的相同条件下形成的磁场加强，从而降低激磁电流、云南曲靖附近铜损和铁损，提高能量转化效率。而且，铁芯总磁化强度为其磁感与面积的乘积，所以铁芯Bm提高，截面积可相应缩小，这使铁芯、云南曲靖附近铜线质量减轻，从而降低电器的铁损和成本。无取向硅钢的磁感保证值取B50，即5000A/m磁场下的磁感强度，而取向硅钢磁感则取B8，磁感单位为Tesla。不同电工钢的采用的磁感应强度标准不同，

电工钢硅钢片Electrical steel, also known as silicon steel sheet, is an indispensable metal material in the power, electronics, and military industries, and is also the largest functional material in production. It is mainly used as the iron core for various motors, generators, and transformers. Since it is a functional material, its performance testing also revolves around "function". These indicators are often mentioned in trade and processing processes, and a brief understanding can help everyone better carry out their work. The performance testing of electrical steel mainly includes the following aspects: magnetic inspection, stacking coefficient inspection, coating adhesion inspection, repeated bending inspection, size and shape surface inspection, and conventional mechanical property inspection. In addition to the types of products listed above, there are also some special purpose electrical steel plates, such as 0.15 and 0.20mm thick 3％ Si cold-rolled non oriented silicon steel strips and 0.025, 0.05, and 0.1mm thick 3％ Si cold-rolled oriented silicon steel strips, which are used as intermediate and intermediate grade High frequency motors and transformers, as well as pulse transformers, etc； 0.7mm thick 3％ Si high-strength cold-rolled non oriented silicon steel plate for relays and power switches； High strength cold-rolled electrical steel plate for new high-speed motor rotors； Low carbon electrical steel hot-rolled thick and cold-rolled plates for magnetic shielding and high-energy accelerator electromagnets such as medical magnetic resonance tomography scanners； 4.5％ to 6.5％ Si high silicon steel plates for high-frequency motors, transformers, and magnetic shielding. Generally, motors, transformers, and other electrical components are required to have high efficiency, low power consumption, small size, and light weight. Electrical steel plates are usually guaranteed to have magnetic properties based on core loss and magnetic induction strength. Magnetic induction strength is the number of magnetic lines passing through a unit cross-sectional area of the iron core, also known as magnetic flux density. It represents the material‘s magnetization ability, measured in T. The magnetic induction strength of electrical steel plates is high, and the excitation current (also known as no-load current) of the iron core is reduced. Copper and iron losses are also reduced, which can save electrical energy. When the power of the motor and transformer remains constant, the magnetic induction intensity is high, and the design Bm can be increased. The cross-sectional area of the iron core can be reduced, which reduces the volume and weight of the iron core, and saves the amount of electrical steel plates, wires, insulation materials, and structural materials used. This can reduce the total loss and manufacturing cost of the motor and transformer, and is beneficial for the manufacturing, installation, and transportation of large transformers and motors. The main requirements for the performance of silicon steel are: 1. Low iron loss is the most important indicator of the quality of silicon steel sheets. Various countries classify grades based on iron loss values, with the lower the iron loss, the higher the grade. 2. Under strong magnetic fields, the magnetic induction intensity (magnetic induction) is high, which reduces the volume and weight of the iron core of the motor and transformer, saving silicon steel sheets, copper wires, and insulation materials. 3. The surface is smooth, flat, and the thickness is uniform, which can improve the filling coefficient of the iron core. 4. Good lamination performance is more important for manufacturing micro and small electric motors. 5. The adhesion and weldability of the surface insulation film are good, which can prevent corrosion and improve the punching performan